Polymer | Thickness d [nm] | Linear polarization | Circular polarization | ||||||
---|---|---|---|---|---|---|---|---|---|
30 min | 60 min | 30 min | 60 min | ||||||
Λ[nm] | h [nm] | Λ[nm] | h [nm] | Λ[nm] | h [nm] | Λ[nm] | h [nm] | ||
1 | 101 | 401.9 ±2.4 | 51 | 406.3 ±1.1 | 51 | 412.7 ±2.4 | 68 | 420.6 ±1.4 | 58 |
493 | 434.9 ±1.3 | 214 | 930.5 ±9.4 | 270 | 412.9 ±2.3 | 168 | 1472.5 ±31.3 | 293 | |
2 | 580 | 412.7 ±0.9 | 22 | ||||||
3 | 886 | 440.6 ±3.7 | 70 |